[1]马亚飞,苏小超,郭忠照,等.锈胀钢筋混凝土梁疲劳性能试验研究[J].自然灾害学报,2017,(06):061-68.[doi:10.13577/j.jnd.2017.0607]
 MA Yafei,SU Xiaochao,GUO Zhongzhao,et al.Experimental study on fatigue behavior of reinforced concrete beams with corrosion-induced cracking[J].,2017,(06):061-68.[doi:10.13577/j.jnd.2017.0607]
点击复制

锈胀钢筋混凝土梁疲劳性能试验研究
分享到:

《自然灾害学报》[ISSN:/CN:23-1324/X]

卷:
期数:
2017年06期
页码:
061-68
栏目:
出版日期:
2017-12-08

文章信息/Info

Title:
Experimental study on fatigue behavior of reinforced concrete beams with corrosion-induced cracking
作者:
马亚飞 苏小超 郭忠照 王磊 张建仁
长沙理工大学 土木工程学院, 湖南 长沙 410114
Author(s):
MA Yafei SU Xiaochao GUO Zhongzhao WANG Lei ZHANG Jianren
School of Civil Engineering, Changsha University of Science & Technology, Changsha 410114, China
关键词:
钢筋混凝土梁疲劳锈胀寿命失效形式
Keywords:
reinforced concrete beamfatiguecorrosion-induced crackinglifefailure mode
分类号:
TU375.1;U447;X9
DOI:
10.13577/j.jnd.2017.0607
摘要:
为研究锈胀对钢筋混凝土梁疲劳性能的影响,采用电化学快速锈蚀试验得到了不同锈胀程度的钢筋混凝土梁,讨论了初始锈胀裂缝的宽度及分布情况。开展了钢筋混凝土梁的静力及疲劳试验,研究了不同疲劳循环次数后梁的荷载-挠度关系、混凝土疲劳裂缝发展、疲劳寿命及失效模式。试验结果表明:相同静载水平下梁的跨中挠度随疲劳循环的增加而增大,经历相同疲劳循环后梁的刚度退化对锈胀程度敏感性大;锈胀钢筋混凝土梁混凝土裂缝数量减少、裂缝平均间距增大,锈胀程度较低梁的混凝土疲劳裂缝发展具有明显的"三阶段"特征;疲劳试验梁均发生了以纵向主筋疲劳断裂为主要标志的脆性失效形式;锈胀降低钢筋混凝土梁的疲劳寿命,锈胀引起混凝土剥离梁的疲劳寿命下降90%以上。
Abstract:
This paper aims to study the effect of corrosion-induced cracking on the fatigue behavior of reinforced concrete beams. An accelerated corrosion test is performed to obtain different cracking reinforced concrete beams. The initial crack width and crack distribution are discussed. Static loading tests and fatigue tests are conducted. The load-deflection relationship, fatigue crack propagation of concrete, fatigue life and failure mode after various fatigue cycles are analyzed. The experimental results show that the deflection in mid-span increases with the increase of fatigue cycles under the same load level. The stiffness of beam is sensitive to corrosion crack degree after the beams are subjected to a same fatigue cycle. For the beam with corrosion cracks, the number of concrete fatigue cracks decreases and the average crack spacing increases. A key feature of "three stage" is presented in concrete fatigue crack propagation for the beam with a lower crack degree. All the beams occur a brittle failure as fatigue fracture of reinforcing bars. Corrosion crack decreases the fatigue life of reinforced concrete beam. The decreased ratio of fatigue life for the beam with concrete spalling is about 90% of uncorroded beam.

参考文献/References:

[1] Ma Y, Zhang J, Wang L, et al. Probabilistic prediction with bayesian updating for strength degradation of RC bridge beams[J]. Structural Safety, 2013, 44:102-109.
[2] 马亚飞, 王磊, 张建仁. 氯盐环境下钢筋混凝土构件锈胀开裂风险概率分析[J]. 自然灾害学报, 2012, 21(4):207-215. MA Yafei, WANG Lei, ZHANG Jianren. Risk probability analysis of chloride-induced corrosion cracking of reinforced concrete member[J]. Journal of Natural Disasters, 2012, 21(4):207-215. (in Chinese)
[3] Apostolopoulos C, Papadopoulos M. Tensile and low cycle fatigue behavior of corroded reinforcing steel bars S400[J]. Construction and Building Materials, 2007, 21(4):855-864.
[4] Apostolopoulos C. Mechanical behavior of corroded reinforcing steel bars S500s tempcore under low cycle fatigue[J]. Construction and Building Materials, 2007, 21(7):1447-1456.
[5] ZHANG W, SONG X, GU X, et al. Tensile and fatigue behavior of corroded rebars[J]. Construction and Building Materials, 2012, 34:409-417.
[6] Li H, Lan C, Ju Y, et al. Experimental and numerical study of the fatigue properties of corroded parallel wire cables[J]. Journal of Bridge Engineering, 2011, 17(2):211-220.
[7] Nakamura S, Suzumura K. Experimental study on fatigue strength of corroded bridge wires[J]. Journal of Bridge Engineering, 2012, 18(3):200-209.
[8] Yi W, Kunnath SK, Sun X, et al. Fatigue behavior of reinforced concrete beams with corroded steel reinforcement[J]. ACI Structural Journal, 2010, 107(5):526-533.
[9] 王海超, 贡金鑫, 宋元成. 钢筋混凝土梁腐蚀疲劳的试验研究[J]. 建筑结构学报, 2005, 25(5):105-110. WANG Haichao, GONG Jinxin, SONG Yuancheng. Experimental study on corrosion fatigue of RC beams[J]. Journal of Building Structures, 2005, 25(5):105-110. (in Chinese)
[10] 李士彬, 汤红卫, 张鑫, 等. 锈蚀钢筋混凝土梁的疲劳性能[J]. 四川大学学报(工程科学版), 2014, 46(3):154-160. LI Shibin, TANG Hongwei, ZHANG Xin, et al. Fatigue behavior of corroded reinforced concrete beams[J]. Journal of Sichuan University(Engineering Science Edition), 2014, 46(3):154-160. (in Chinese)
[11] 吴瑾, 王晨霞, 徐贾, 等. 疲劳荷载下锈蚀钢筋混凝土梁弯曲性能试验研究[J]. 土木工程学报, 2012, 45(10):118-124. WU Jin, WANG Chenxia, XU Jia, et al. Study on flexural behavior of corroded reinforced concrete beams under fatigue loads[J]. China Civil Engineering Journal, 2012, 45(10):118-124. (in Chinese)
[12] Sun J, Huang Q, Ren Yuan. Performance deterioration of corroded RC beams and reinforcing bars under repeated loading[J]. Construction and Building Materials, 2015, 96:404-415.
[13] Tilly G. Durability of concrete bridges[J]. Highways and transportation, 1988, 35(2):10-19.
[14] Dicleli M, Bruneau M. Fatigue-based methodology for managing impact of heavy-permit trucks on steel highway bridges[J]. Journal of Structural Engineering, 1995, 121(11):1651-1659.
[15] Liu Y, MahadevanS. Stochastic fatigue damage modeling under variable amplitude loading[J]. International Journal of Fatigue, 2007, 29:1149-1161.
[16] Bastidas-Arteaga E, Bressolette P, Chateauneuf A, et al. Probabilistic lifetime assessment of RC structures under coupled corrosion-fatigue deteriorationprocesses[J]. Structural Safety, 2009, 31(1):84-96.
[17] Ma Y, Xiang Y, Wang L, et al. Fatigue life prediction for aging RC beams considering corrosive environments[J]. Engineering Structures, 2014, 79:211-221.
[18] 姬永生, 张博雅, 张领雷, 等. 钢筋锈层发展和锈蚀量分布模型比较研究[J]. 中国矿业大学学报, 2012, 41(3):355-360. JI Yongsheng, ZHANG Boya, ZHANG Ling, et al. Propagation of the corrosion layer and model of corrosion distribution on steel re-enforcing bar in concrete[J]. Journal of China University of Mining & Technology, 2012, 41(3):355-360. (in Chinese)

相似文献/References:

[1]白丽丽,王振清,苏娟,等.火灾后钢筋混凝土梁的抗弯可靠性[J].自然灾害学报,2009,(01):095.
 BAI Li-li,WANG Zhen-qing,SU Juan,et al.Bending reliability of RC beam after fire exposure[J].,2009,(06):095.
[2]董宏英,王超超,陈桂林,等.高强再生混凝土梁抗弯性能试验研究[J].自然灾害学报,2016,(02):187.[doi:10.13577/j.jnd.2016.0223]
 DONG Hongying,WANG Chaochao,CHEN Guilin,et al.Experimental study on flexural behavior of high strength recycled concrete beams[J].,2016,(06):187.[doi:10.13577/j.jnd.2016.0223]

备注/Memo

备注/Memo:
收稿日期:2016-11-01;改回日期:2017-01-01。
基金项目:国家自然科学基金(51508036,51478050);国家重点基础研究发展计划(973计划)(2015CB057705);湖南省自然科学基金(2017JJ3325)
作者简介:马亚飞(1984-),男,讲师,博士,主要从事桥梁可靠性及耐久性评估研究.E-mail:yafei.ma@csust.edu.cn
更新日期/Last Update: 1900-01-01